WebCalculate (a) the activation energy; and (b) the constant D0. Solution: 6 × 10−15 D0 exp [−Q/ (1.987)/ (1000)] = 1× 10−9 D0 exp [−Q/ (1.987)/ (1673)] 6 × 10–6 = exp [–Q (0.00050327 – 0.00030082)] = exp [–0.00020245 Q] –12.0238 = −0.00020245 Q or Q = 59,390 cal/mol 1 × 10–9 = D0 exp [–59,390/ (1.987)/ (1673)] D0 = 0.057 cm 2 /s WebDetermine the carburizing time necessary to achieve a carbon concentration of 0.45 wt% at a position 2 mm into an iron-carbon alloy that initially contains 0.20 wt% C. The surface concentration is to be maintained at 1.30 wt% C, and the treatment is to be conducted at 1000 °C. Use the diffusion data for y-Fe. 13.
Answered: 13. Determine the carburizing time… bartleby
WebEnter the email address you signed up with and we'll email you a reset link. WebDetermine the carburizing time necessary to achieve a carbon concentration of 0.45 wt% at a position 2-mm into a steel alloy that initially contains 0.20 wt% carbon.The surface concentration is to be maintained at 1.30 wt% at 1000℃.Use table 5-4 for error function values as needed. Expert Solution Want to see the full answer? dunmow bi folding doors
ME 210 Materials Science Chapter 7 Problem Set
WebDetermine the carburizing time necessary to achieve a carbon concentration of 0.45 w t % at a position 2 m m into an iron-carbon alloy that initially contains 0.20 w t % C. The surface concentration is to be maintained at 1.30 w t % C, and the treatment is to be conducted at 1000 ∘ C. Use the diffusion data for γ -Fe in Table 5.2. Check back soon! WebDetermine the carburizing time necessary to achieve a carbon concentration of 0.45 wt% at a position 2 mm into an iron?carbon alloy that initially contains 0.20 wt% C. The surface concentration is to be maintained at 1.30 wt% C, and the treatment is to be conducted at 1000?C. Use the diffusion data for g-Fe in Table 5.2. Transcribed Image Text: Web1. Determine the carburizing time necessary to achieve a carbon concentration of 0.40 wt% at a position 2 mm into an iron-carbon alloy that initially contains 0.20 wt% C. The surface concentration is to be maintained at 1.20 wt% C, dnd the treatment is to be conducted at 1000°C. dunmow broadcast announcements